温度
|
重度γ |
导热系数λ |
粘度μ×104 |
热焓i |
普兰特系数Pr |
|
℃
|
kgf/m3 |
kcal/(m.h.℃) |
(kg.s)/m2 |
kcal/kg |
数 |
|
150
|
1976 |
0.379 |
18.12 |
80.7 |
57.4 |
|
160
|
1967 |
0.378 |
14.95 |
84.1 |
47.5 |
|
170
|
1959 |
0.377 |
12.53 |
87.5 |
39.9 |
|
180
|
1951 |
0.376 |
10.68 |
90.9 |
34.1 |
|
190
|
1943 |
0.375 |
9.21 |
94.3 |
29.5 |
|
200
|
1934 |
0.374 |
8.04 |
97.7 |
25.8 |
|
210
|
1926 |
0.373 |
7.09 |
101.1 |
22.8 |
|
220
|
1919 |
0.372 |
6.31 |
104.5 |
20.4 |
|
230
|
1911 |
0.370 |
5.67 |
107.9 |
18.4 |
|
240
|
1903 |
0.368 |
5.12 |
111.3 |
16.7 |
| 250 |
1895 |
0.366 |
4.66 |
114.7 |
15.3 |
| 260 |
1887 |
0.360 |
4.27 |
118.1 |
14.2 |
| 270 |
1879 |
0.355 |
3.93 |
121.5 |
13.3 |
| 280 |
1871 |
0.350 |
3.63 |
124.9 |
12.4 |
| 290 |
1864 |
0.344 |
3.38 |
128.3 |
11.8 |
| 300 |
1856 |
0.338 |
3.15 |
131.7 |
11.2 |
| 320 |
1841 |
0.328 |
2.77 |
138.5 |
10.1 |
| 340 |
1826 |
0.317 |
2.48 |
145.3 |
9.39 |
| 360 |
1812 |
0.306 |
2.23 |
152.1 |
8.74 |
| 380 |
1797 |
0.295 |
2.04 |
158.9 |
8.30 |
| 400 |
1783 |
0.284 |
1.871 |
165.7 |
7.91 |
| 420 |
1769 |
0.273 |
1.730 |
172.5 |
7.60 |
| 440 |
1755 |
0.262 |
1.610 |
179.3 |
7.37 |
| 460 |
1741 |
0.251 |
1.507 |
186.1 |
7.20 |
| 480 |
1728 |
0.240 |
1.418 |
192.9 |
7.09 |
| 500 |
1715 |
0.229 |
1.339 |
199.7 |
7.02 |
一、应用范围：
本产品广泛用于冶金、化工、木材等行业，在熔盐炉中使用，温度可达到５００℃。
二、使用说明：
该产品在槽内可直接加热熔解或在超高温热载体中加少量水，加热使之熔解。熔解到粘度足可以用循环泵打循环后，送至载热炉逐步循环升温，达到目标温度。
三、注意事项：
１.开始升温时，严格控制升温速度，尽量避免系统运行中急冷急热。
２.在系统中使用，需正压状态。
３.在高温使用中，严禁水和有机类物质混入。
４.在循环加热中流速恒定，不能超过膜温。
５.当超高温热载体出现多时沉淀物时，应更换热载体。
|